LNP™ THERMOCOMP™ Compound D151RCC

Sustainable Grade

LNP THERMOCOMP D151RCC compound is based on recycled Polycarbonate (PC) resin containing 10% glass fiber. Added features of this grade include: High Modulus, Good Surface, Low Warpage, Good Ductility, Non-Brominated & Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) Polycarbonate content up to 50%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Flame Retardant
High stiffness/Strength
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Commercial Appliance
Electrical
Home Appliances

Applications

Possible usage of material

Mobile Phone
Electronic Components
Personal Computing
Wearables
consumer electric housing
mobile phone enclosure
laptop housing
wearable device housing
tablet pc housing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+16	Ω	ASTM D257
Volume Resistivity	1.E+16	Ω.cm	ASTM D257
Dielectric Constant, 1.1 GHz	3	-	SABIC method
Dielectric Constant, 1.9 GHz	3.05	-	SABIC method
Dielectric Constant, 5 GHz	3.04	-	SABIC method
Dielectric Constant, 10 GHz	2.99	-	SABIC method
Dissipation Factor, 1.1 GHz	0.007	-	SABIC method
Dissipation Factor, 1.9 GHz	0.007	-	SABIC method
Dissipation Factor, 5 GHz	0.007	-	SABIC method
Dissipation Factor, 10 GHz	0.007	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥0.6	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	120	J/m	ASTM D256
Izod Impact, notched, -30°C	62	J/m	ASTM D256
Izod Impact, unnotched, 23°C	680	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	755	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	23	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	5	J	ASTM D3763
*Izod Impact, notched 80103 +23°C*	12	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	41	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	43	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	42	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	44	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	11	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	6	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	47	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	51	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	11	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	6	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	50	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	51	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Nozzle Temperature	285 - 305	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	81	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	78	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	3.2	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.5	%	ASTM D638
Tensile Modulus, 5 mm/min	4320	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	132	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4100	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	81	MPa	ISO 527
Tensile Stress, break, 5 mm/min	78	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.1	%	ISO 527
Tensile Strain, break, 5 mm/min	3.5	%	ISO 527
Tensile Modulus, 1 mm/min	4320	MPa	ISO 527
Flexural Strength, 2 mm/min	128	MPa	ISO 178
Flexural Modulus, 2 mm/min	3900	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.27	-	ASTM D792
Melt Flow Rate, 300°C/1.2 kgf	13	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/2.16 kgf	27.7	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	12	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg	25.2	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.04	%	ISO 62-1
Mold Shrinkage, flow	0.32	%	SABIC method
Mold Shrinkage, xflow	0.42	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	120	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	114	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	119	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	113	°C	ISO 75/Af
CTE, 23°C to 80°C, flow	3.7E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, xflow	7.6E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	3.1E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	5.4E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	3.9E-5	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.6E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, flow	3.2E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	5.9E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	121	°C	ISO 306
Vicat Softening Temp, Rate B/120	123	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection