FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1 | mm | UL 94 |
LNP THERMOCOMP D551RC compound is based on recycled Polycarbonate (PC) resin containing 50% glass fiber. Added features of this grade include: High Modulus, Low Warpage, Good Ductility, Non-Brominated & Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) Polycarbonate content up to 30%.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 423 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 119 | J/m | ASTM D256 |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 31 | kJ/m² | ISO 179/1eU |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 110 | °C | |
Drying Time | 3 - 6 | Hrs | |
Drying Time (Cumulative) | 12 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 285 - 310 | °C | |
Nozzle Temperature | 285 - 305 | °C | |
Front - Zone 3 Temperature | 280 - 300 | °C | |
Middle - Zone 2 Temperature | 270 - 290 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.1 - 0.3 | MPa | |
Screw Speed | 50 - 90 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 16090 | MPa | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 13420 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 147 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.35 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 15270 | MPa | ISO 527 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.618 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.05 - 0.2 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.05 - 0.2 | % | ASTM D955 |
Melt Volume Rate, MVR at 300°C/2.16 kg | 20 | cm³/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 300°C/5.0 kg | 34.98 | cm³/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.31E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 4.24E-05 | 1/°C | ASTM E831 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature