LNP™ THERMOCOMP™ Compound D551RCC

Sustainable Grade

LNP THERMOCOMP COMPOUND D551RCC is a compound based on Recycle Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include high modulus, good flatness, good impact performance, Non-Brominated & Non-Chlorinated Flame Retardant. Post-Consumer Recycling (PCR) polycarbonate content up to 25%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Flame Retardant
High stiffness/Strength
Sustainable (Mechanical Recycling)

Industry

Material previously used in

Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Components
Personal Computing
Wearables
consumer electric housing
mobile phone enclosure
laptop housing
wearable device housing
tablet pc housing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+16	Ω	ASTM D257
Volume Resistivity	1.E+15	Ω.cm	ASTM D257
Dielectric Constant, 1.1 GHz	3.92	-	SABIC method
Dielectric Constant, 1.9 GHz	3.98	-	SABIC method
Dielectric Constant, 5 GHz	3.97	-	SABIC method
Dielectric Constant, 10 GHz	3.95	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0069	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0073	-	SABIC method
Dissipation Factor, 5 GHz	0.0079	-	SABIC method
Dissipation Factor, 10 GHz	0.0083	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥1.0	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	120	J/m	ASTM D256
Izod Impact, notched, -30°C	110	J/m	ASTM D256
Izod Impact, unnotched, 23°C	407	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	424	J/m	ASTM D4812
*Izod Impact, notched 80103 +23°C*	12	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	38	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	43	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	12	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	35	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	41	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	13	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	12	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	41	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	46	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	12	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	11	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	38	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	44	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	22	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	14	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 6	Hrs
Drying Time (Cumulative)	12	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Nozzle Temperature	285 - 305	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	151	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D638
Tensile Modulus, 5 mm/min	15500	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	220	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	13500	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	150	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	15700	MPa	ISO 527
Flexural Strength, 2 mm/min	214	MPa	ISO 178
Flexural Modulus, 2 mm/min	14100	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.63	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.01	%	ISO 62-1
Melt Flow Rate, 300°C/1.2 kgf	16	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/2.16 kgf	33	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	10	cm³/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/2.16 kg	22	cm³/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/5.0 kg	42	cm³/10 min	ASTM D1238
Mold Shrinkage, flow	0.08	%	SABIC method
Mold Shrinkage, xflow	0.13	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	112	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	103	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	113	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	104	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	1.3E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	4.2E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	1.4E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, xflow	5.3E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.3E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.6E-5	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow	1.3E-5	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	5.7E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	109	°C	ISO 306
Vicat Softening Temp, Rate B/120	111	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES