LNP THERMOCOMP DB008ERP compound is based on Polycarbonate (PC) resin containing 40% glass bead. Added features of this grade include: Easy Molding, Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-1 Flame Class Rating | ≥3 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 400 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 300 - 315 | °C | |
| Front - Zone 3 Temperature | 310 - 320 | °C | |
| Middle - Zone 2 Temperature | 305 - 315 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 42 | MPa | ASTM D638 |
| Tensile Strain, break | 3.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3960 | MPa | ASTM D638 |
| Flexural Stress | 75 | MPa | ASTM D790 |
| Flexural Modulus | 3840 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.7 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.67 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.73 | % | ISO 294 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D648 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |