FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.8 | mm | UL 94 |
LNP THERMOCOMP DC0041PR compound is based on Polycarbonate (PC) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, Non-Brominated, Non-Chlorinated Flame Retardant, PCR content up to 30%.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.8 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 400 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 55 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 9 | J | ASTM D3763 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 70 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 275 - 310 | °C | |
Front - Zone 3 Temperature | 280 - 300 | °C | |
Middle - Zone 2 Temperature | 270 - 290 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Mold Temperature | 60 - 80 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 63 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 160 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 1.1 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 19000 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 200 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 17500 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.32 | - | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.08 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.33 | % | ASTM D955 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D648 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
Your PDF is downloading. Please wait.