LNP™ THERMOCOMP™ Compound DF0021XQ

LNP THERMOCOMP DF0021XQ compound is based on Polycarbonate (PC) resin containing 10% glass fiber. Added features of this grade include: High Modulus, Good Surface, Low Warpage, Good Ductility, Non-Brominated & Non-Chlorinated Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Impact resistant
Low Warpage
Non Cl/Br flame retardant

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Mobile Phone
Wearables
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.05	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0067	-	SABIC method
Dielectric Constant, 1.9 GHz	3.04	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0063	-	SABIC method
Dielectric Constant, 5 GHz	3	-	SABIC method
Dissipation Factor, 5 GHz	0.0064	-	SABIC method
Dielectric Constant, 10 GHz	2.97	-	SABIC method
Dissipation Factor, 10 GHz	0.0063	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	150	J/m	ASTM D256
Izod Impact, notched, -30°C	80	J/m	ASTM D256
Izod Impact, unnotched, 23°C	710	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	850	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	16	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	46	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80103 +23°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	48	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	55	kJ/m²	ISO 180/1U
Charpy
– 23°C, V-notch Edgew 80104 sp=62mm	16	kJ/m²	ISO 179/1eA
– -30°C, V-notch Edgew 80104 sp=62mm	7	kJ/m²	ISO 179/1eA
– 23°C, Unnotch Edgew 80104 sp=62mm	53	kJ/m²	ISO 179/1eU
– -30°C, Unnotch Edgew 80104 sp=62mm	63	kJ/m²	ISO 179/1eU
– 23°C, V-notch Edgew 80103 sp=62mm	16	kJ/m²	ISO 179/1eA
– -30°C, V-notch Edgew 80103 sp=62mm	7	kJ/m²	ISO 179/1eA
– 23°C, Unnotch Edgew 80103 sp=62mm	54	kJ/m²	ISO 179/1eU
– -30°C, Unnotch Edgew 80103 sp=62mm	63	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Energy @ peak, 23°C	26	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	270 - 295	°C
Nozzle Temperature	270 - 295	°C
Front - Zone 3 Temperature	270 - 295	°C
Middle - Zone 2 Temperature	260 - 280	°C
Rear - Zone 1 Temperature	250 - 270	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 90	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	82	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.5	%	ASTM D638
Tensile Modulus, 5 mm/min	4450	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	133	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4150	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	82	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3.5	%	ISO 527
Tensile Modulus, 1 mm/min	4450	MPa	ISO 527
Flexural Strength, 2 mm/min	135	MPa	ISO 178
Flexural Modulus, 2 mm/min	4020	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.27	-	ASTM D792
Melt Flow Rate, 300°C/1.2 kgf	18	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/2.16 kgf	34.5	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	16.5	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg	32	cm³/10 min	ISO 1133
Water Absorption, (23°C/saturated)	0.09	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.6	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.5 - 0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	119	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	119	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	114	°C	ISO 75/Af
CTE, 23°C to 80°C, flow	4.00E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.00E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	127	°C	ISO 306
Vicat Softening Temp, Rate B/50	121	°C	ISO 306
Vicat Softening Temp, Rate B/120	123	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES