LNP™ THERMOCOMP™ Compound DF004EXP

LNP THERMOCOMP DF004EXP compound is based on Polycarbonate (PC) resin containing 20% glass fiber. Added features of this grade include: Easy Molding.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Building Component
Electrical
Industrial General
Personal Accessory

Applications

Possible usage of material

Displays
Document Handling
Medical Device
Traffic Management

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	690	J/m	ASTM D4812
Izod Impact, notched, 23°C	62	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	54	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.02 - 0.03	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	4552	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	67	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	7	%	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	126	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4050	MPa	ASTM D790
Tensile Modulus, 1 mm/min	4632	MPa	ISO 527
Tensile Stress, break, 5 mm/min	70	MPa	ISO 527
Tensile Strain, break, 5 mm/min	5	%	ISO 527
Flexural Modulus, 2 mm/min	4578	MPa	ISO 178
Flexural Stress, break, 2 mm/min	128	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.36	-	ASTM D792
Density	1.36	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24 hrs)	-0.0073	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.07	%	ISO 62-1
Mold Shrinkage, flow, 24 hrs	0.14	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.21	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	153	°C	ISO 306
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	136	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience