LNP THERMOCOMP DF006 compound is based on Polycarbonate (PC) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 2 | ≥3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥1.5 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 914 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 155 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 58 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8630 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 180 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8100 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 122 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8100 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 185 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7200 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.45 | - | ASTM D792 |
| Density | 1.44 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.07 | % | ASTM D570 |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 144 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 140 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 146 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 115 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.