LNP THERMOCOMP DF0081PI compound is based on Polycarbonate (PC) resin containing 40% glass fiber. Added features of this grade include: High Modulus, Improved Impact, Low Warpage, Non-Brominated & Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.2 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating | ≥1 | mm | UL 94 |
| UL Recognized, 94V-2 Flame Class Rating | ≥0.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 264 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 81 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 10 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 22 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 285 - 310 | °C | |
| Nozzle Temperature | 285 - 305 | °C | |
| Front - Zone 3 Temperature | 280 - 300 | °C | |
| Middle - Zone 2 Temperature | 270 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 280 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.1 - 0.3 | MPa | |
| Screw Speed | 50 - 90 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 130 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 12700 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 10000 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 123 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12500 | MPa | ISO 527 |
| Flexural Strain, break, 2 mm/min | 1.9 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 10800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow | 0.4 | % | SABIC method |
| Mold Shrinkage, xflow | 0.41 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 110 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |