FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.6 | mm | UL 94 |
LNP THERMOCOMP DX06313 compound is based on Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Impact Modified, Thin-Wall Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.6 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
Izod Impact, notched, 23°C (Natural & Black Colors) | 190 | J/m | ASTM D256 |
Izod Impact, notched, 23°C (Light & White Colors) | 90 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 24 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 12 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 315 - 340 | °C | |
Nozzle Temperature | 310 - 330 | °C | |
Front - Zone 3 Temperature | 315 - 340 | °C | |
Middle - Zone 2 Temperature | 305 - 325 | °C | |
Rear - Zone 1 Temperature | 295 - 315 | °C | |
Mold Temperature | 80 - 115 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 99 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 3.6 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7500 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 170 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 7000 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 3.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7420 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 170 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 6650 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.42 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.5 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 4.6 | g/10 min | ASTM D1238 |
Melt Flow Rate, 300°C/5.0 kgf | 42 | g/10 min | ASTM D1238 |
Density | 1.42 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.4 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/5.0 kg | 32 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 142 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 136 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 2.2E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 142 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.