IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 747 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
LNP THERMOCOMP DX06411 compound is based on Polycarbonate (PC) resin containing 20% glass fiber. Added features of this grade include: Easy Molding, Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 747 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 305 - 325 | °C | |
Front - Zone 3 Temperature | 320 - 330 | °C | |
Middle - Zone 2 Temperature | 310 - 320 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 82 | MPa | ASTM D638 |
Tensile Strain, break | 4.2 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 5740 | MPa | ASTM D638 |
Flexural Stress | 144 | MPa | ASTM D790 |
Flexural Modulus | 5650 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.4 | g/cm³ | ASTM D792 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D648 |