LNP™ THERMOCOMP™ Compound EC006E

LNP THERMOCOMP EC006E compound is based on Polyetherimide (PEI) resin containing 30% carbon fiber. Added features of this grade include: Easy Molding, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Good Processability
High stiffness/Strength
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Instrumented Dart Impact Energy @ peak, 23°C	6	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	34	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 400	°C
Rear - Zone 1 Temperature	360 - 380	°C
Middle - Zone 2 Temperature	370 - 390	°C
Front - Zone 3 Temperature	380 - 400	°C
Nozzle Temperature	390 - 400	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	230	MPa	ASTM D638
Tensile Strain, break	1.5	%	ASTM D638
Tensile Modulus, 50 mm/min	23300	MPa	ASTM D638
Flexural Stress	314	MPa	ASTM D790
Flexural Modulus	19160	MPa	ASTM D790
Tensile Stress, break	215	MPa	ISO 527
Tensile Strain, break	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	18470	MPa	ISO 527
Flexural Stress	306	MPa	ISO 178
Flexural Modulus	20800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.394	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.17	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.1	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.1	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.51	%	ISO 294
Wear Factor Washer	75	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.52	-	ASTM D3702 Modified: Manual
Static COF	0.48	-	ASTM D3702 Modified: Manual
Density	1.39	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	206	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	208	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES