LNP™ THERMOCOMP™ Compound EC006PXQ

LNP THERMOCOMP EC006PXQ compound is based on Polyetherimide (PEI) resin containing 30% carbon fiber. Added features of this grade include: Electrically Conductive, Exceptional Processing, FAR25.853 Compliant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Flame Retardant
High Flow
High stiffness/Strength
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

Aerospace
Automotive Under the Hood
Building Component
Electrical
Sport/Leisure

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+03	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	581	J/m	ASTM D4812
Izod Impact, notched, 23°C	81	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	12	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 400	°C
Rear - Zone 1 Temperature	360 - 380	°C
Middle - Zone 2 Temperature	370 - 390	°C
Front - Zone 3 Temperature	380 - 400	°C
Nozzle Temperature	390 - 400	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Flexural Stress, break, 2 mm/min	334	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	272	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.3 - 1.4	%	ASTM D638
Tensile Modulus, 5 mm/min	29520	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	341	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	23800	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	248	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	27560	MPa	ISO 527
Flexural Modulus, 2 mm/min	23060	MPa	ISO 178
Compressive Strength	244	MPa	SABIC method
Shear Modulus	4726	MPa	ASTM D732
Shear Strength	128	MPa	ASTM D732

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.39	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.11	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.1 - 0.6	%	ASTM D955
Melt Flow Rate, 380°C/6.7 kgf	22	g/10 min	ASTM D1238
Poisson's Ratio	0.44	-	ASTM E132

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	195	°C	ASTM D648
CTE, -40°C to 150°C, flow	7.2E-06	1/°C	ASTM E831
CTE, -40°C to 150°C, xflow	5.8E-05	1/°C	ASTM E831

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards