LNP™ THERMOCOMP™ Compound EX06430H

LNP THERMOCOMP EX06430H compound is based on Polyetherimide (PEI) resin containing mineral. Added features of this grade include: Healthcare, X-Ray Detectable.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Healthcare/Formula lock
High temperature resistance
No PFAS intentionally added
X-Ray and metal detection

Industry

Material previously used in

General Healthcare
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Monitoring and Imaging
Surgical Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1383	J/m	ASTM D4812
Izod Impact, notched, 23°C	48	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	10	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	73	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 400	°C
Rear - Zone 1 Temperature	360 - 380	°C
Middle - Zone 2 Temperature	370 - 390	°C
Front - Zone 3 Temperature	380 - 400	°C
Nozzle Temperature	390 - 400	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	110	MPa	ASTM D638
Tensile Stress, break	90	MPa	ASTM D638
Tensile Strain, yield	6.7	%	ASTM D638
Tensile Strain, break	13.5	%	ASTM D638
Tensile Modulus, 50 mm/min	3660	MPa	ASTM D638
Flexural Modulus	3660	MPa	ASTM D790
Tensile Stress, yield	106	MPa	ISO 527
Tensile Stress, break	90	MPa	ISO 527
Tensile Strain, yield	6	%	ISO 527
Tensile Strain, break	10.8	%	ISO 527
Tensile Modulus, 1 mm/min	3500	MPa	ISO 527
Flexural Stress	133	MPa	ISO 178
Flexural Modulus	3500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.34 - 1.4	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.7	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.8	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	195	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	194	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES