LNP THERMOCOMP EX11414 compound is based on Polyetherimide (PEI) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, FAR25.853 Compliant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+04 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 598 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 78 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 360 - 400 | °C | |
| Rear - Zone 1 Temperature | 360 - 380 | °C | |
| Middle - Zone 2 Temperature | 370 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Nozzle Temperature | 390 - 400 | °C | |
| Mold Temperature | 140 - 180 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 230 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 17380 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 308 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 14600 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.33 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.23 | % | ASTM D570 |
| Poisson's Ratio | 0.44 | - | ASTM E132 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 213 | °C | ASTM D648 |