LNP™ THERMOCOMP™ Compound FX10009

LNP THERMOCOMP FX10009 compound is based on Polyethylene (PE) resin containing proprietary fillers. Added features of this grade include: Improved Dielectric Properties.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyethylene, Unspecified (PE, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Enclosures

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dissipation Factor, 1 GHz	0.008	-	IEC 60250
Dissipation Factor, 500 MHz	0.008	-	IEC 60250
Dissipation Factor, 100 MHz	0.009	-	IEC 60250
Relative Permittivity, 1 GHz	13.1	-	IEC 60250
Relative Permittivity, 500 MHz	13.4	-	IEC 60250
Relative Permittivity, 100 MHz	13.6	-	IEC 60250

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	5.5	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3.5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.03	%
Melt Temperature	210 - 215	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	200 - 210	°C
Rear - Zone 1 Temperature	190 - 200	°C
Mold Temperature	15 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	20	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	2550	MPa	ISO 527
Flexural Stress, break, 2 mm/min	15	MPa	ISO 178
Flexural Modulus, 2 mm/min	2750	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate, MVR at 190°C/10.0 kg	7.5	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 220°C/10.0 kg	12.5	cm³/10 min	ISO 1133
Mold Shrinkage, flow	1.5 - 2.0	%	SABIC method
Density	2.50	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.08	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, 23°C to 60°C, flow	1.30E-04	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.50E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	100	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	60	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES