IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP GX94043L compound is based on Polysulfone (PSU) resin containing mineral. Added features of this grade include: Low Extractables.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 360 - 370 | °C | |
Front - Zone 3 Temperature | 350 - 360 | °C | |
Middle - Zone 2 Temperature | 340 - 350 | °C | |
Rear - Zone 1 Temperature | 325 - 340 | °C | |
Mold Temperature | 150 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 72 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 4.3 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 119 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow, 24 hrs | 0.25 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.35 | % | ISO 294 |
Density | 1.45 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 0.28 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 4.7E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 176 | °C | ISO 75/Af |