IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 801 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
LNP THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing 35% Glass Fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 801 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 270 - 275 | °C | |
Front - Zone 3 Temperature | 270 - 280 | °C | |
Middle - Zone 2 Temperature | 260 - 270 | °C | |
Rear - Zone 1 Temperature | 255 - 265 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 150 | MPa | ASTM D638 |
Tensile Strain, yield | 3 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 8890 | MPa | ASTM D638 |
Flexural Stress | 227 | MPa | ASTM D790 |
Flexural Modulus | 8270 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.3 | g/cm³ | ASTM D792 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 198 | °C | ASTM D648 |