FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.5 | mm | UL 94 |
LNP THERMOCOMP JF004 compound is based on Polyethersulfone (PES) resin containing 20% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 413 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
Multiaxial Impact | 4 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 73 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 355 - 370 | °C | |
Front - Zone 3 Temperature | 370 - 380 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Rear - Zone 1 Temperature | 345 - 355 | °C | |
Mold Temperature | 140 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 114 | MPa | ASTM D638 |
Tensile Strain, break | 2.8 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 7350 | MPa | ASTM D638 |
Flexural Stress | 186 | MPa | ASTM D790 |
Flexural Modulus | 6690 | MPa | ASTM D790 |
Tensile Stress, break | 109 | MPa | ISO 527 |
Tensile Strain, break | 2.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7590 | MPa | ISO 527 |
Flexural Stress | 182 | MPa | ISO 178 |
Flexural Modulus | 6410 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.51 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.4 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ISO 294 |
Density | 1.51 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.74 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 413 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
Multiaxial Impact | 4 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 73 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 114 | MPa | ASTM D638 |
Tensile Strain, break | 2.8 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 7350 | MPa | ASTM D638 |
Flexural Stress | 186 | MPa | ASTM D790 |
Flexural Modulus | 6690 | MPa | ASTM D790 |
Tensile Stress, break | 109 | MPa | ISO 527 |
Tensile Strain, break | 2.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7590 | MPa | ISO 527 |
Flexural Stress | 182 | MPa | ISO 178 |
Flexural Modulus | 6410 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.51 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.4 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ISO 294 |
Density | 1.51 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.74 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 355 - 370 | °C | |
Front - Zone 3 Temperature | 370 - 380 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Rear - Zone 1 Temperature | 345 - 355 | °C | |
Mold Temperature | 140 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 118 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 6700 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 175 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 5900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.51 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.1E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Af |