LNP™ THERMOCOMP™ Compound JF004L

LNP THERMOCOMP JF004L compound is based on Polyethersulfone (PES) resin containing 20% glass fiber. Added features of this grade include: Low Extractables

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyethersulfone (PESU)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Food contact
High stiffness/Strength
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

Food & Beverage
Home Appliances
Industrial Packaging
Water Management

Applications

Possible usage of material

Semiconductor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	563	J/m	ASTM D4812
Izod Impact, notched, 23°C	50	J/m	ASTM D256
Multiaxial Impact	2	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	11	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	32	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	355 - 370	°C
Front - Zone 3 Temperature	370 - 380	°C
Middle - Zone 2 Temperature	360 - 370	°C
Rear - Zone 1 Temperature	345 - 355	°C
Mold Temperature	140 - 150	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	98	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	98	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	2.7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.9	%	ASTM D638
Tensile Modulus, 50 mm/min	6360	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	152	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	152	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	6300	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	94	MPa	ISO 527
Tensile Stress, break, 5 mm/min	93	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.1	%	ISO 527
Tensile Strain, break, 5 mm/min	2.1	%	ISO 527
Tensile Modulus, 1 mm/min	6640	MPa	ISO 527
Flexural Stress	149	MPa	ISO 178
Flexural Stress, break, 2 mm/min	148	MPa	ISO 178
Flexural Modulus, 2 mm/min	6300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.54	-	ASTM D792
Density	1.53	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.37	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.6	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.7	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.55	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	216	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	211	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	216	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	210	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience