LNP THERMOCOMP JF004RXP compound is based on Polyethersulfone (PES) resin containing glass fiber. Added features of this grade include: Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Compliant, 94V-0 Flame Class Rating | 0.8 | mm | UL 94 by SABIC-IP |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 355 - 370 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 345 - 355 | °C | |
| Mold Temperature | 140 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 122 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7100 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 6000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.25 - 0.45 | % | SABIC method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 223 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 219 | °C | ISO 75/Af |