LNP THERMOCOMP JF006LZZ compound is based on Polyethersulfone (PES) resin containing 30% glass fiber. Added features of this grade include: Extrusion grade, Low Extractables.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 432 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 12 | J | ASTM D3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 355 - 370 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 345 - 355 | °C | |
| Mold Temperature | 140 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 113 | MPa | ASTM D638 |
| Tensile Strain, break | 1.8 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 9790 | MPa | ASTM D638 |
| Flexural Stress | 178 | MPa | ASTM D790 |
| Flexural Modulus | 9230 | MPa | ASTM D790 |
| Tensile Stress, break | 99 | MPa | ISO 527 |
| Tensile Strain, break | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10190 | MPa | ISO 527 |
| Flexural Stress | 222 | MPa | ISO 178 |
| Flexural Modulus | 9240 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.613 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.36 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.25 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.69 | % | ISO 294 |
| Density | 1.6 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 217 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 212 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 3.63E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 3.01E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.64E-05 | 1/°C | ISO 11359-2 |