IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP JX97000 compound is based on Polyethersulfone (PES) resin containing 30% glass fiber. Added features of this grade include: Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time (Cumulative) | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 355 - 370 | °C | |
Front - Zone 3 Temperature | 370 - 380 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Rear - Zone 1 Temperature | 345 - 355 | °C | |
Mold Temperature | 140 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 139 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 9700 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 183 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 8200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.4 | % | SABIC method |
Density | 1.61 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 2.6E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 224 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Af |