LNP THERMOCOMP KF008A compound is based on POM (Acetal) copolymer resin containing 40% glass fiber.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 41.6 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 175 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 5 mm/min | 11420 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.87 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 69.4 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 12500 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 113 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.71 | - | ASTM D792 |
| Mold Shrinkage, flow | 0.212 | % | SABIC method |
| Mold Shrinkage, xflow | 1.387 | % | SABIC method |