LNP THERMOCOMP KZ006AXP compound is based on POM (Acetal) homopolymer resin containing 30% milled glass.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 180 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 38 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Mold Temperature | 85 - 110 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Strength, 1.3 mm/min, 50 mm span | 72 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4150 | MPa | ASTM D790 |
| Tensile Stress, brk, Type I, 5 mm/min | 45 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.8 - 1 | % | ASTM D955 |
| Water Absorption, (23°C/24hrs) | 0.3 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |