IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP LC008EXP compound is based on Polyetheretherketone (PEEK) resin containing 40% carbon fiber. Added features of this grade include: Electrically Conductive, Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.1 | % | |
Melt Temperature | 380 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 395 | °C | |
Middle - Zone 2 Temperature | 365 - 375 | °C | |
Rear - Zone 1 Temperature | 350 - 360 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 256 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 26200 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 341 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 22900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.45 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 4.E-06 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 4.1E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >300 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature