LNP™ THERMOCOMP™ Compound LF002EXD-WT02005

LNP THERMOCOMP LF002EXD-WT02005 compound is based on Polyetheretherketone (PEEK) resin containing 10% glass fiber. Added features of this grade include Custom Color and Easy Molding.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetheretherketone (PEEK)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
High stiffness/Strength
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

Commercial Appliance
Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Hygiene/Personal Care

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	26	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	4	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	33	kJ/m²	ISO 179/1eU
Izod Impact, unnotched, 23°C	39	J/m	ASTM D4812
Izod Impact, notched, 23°C	378	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.1	%
Hopper Temperature	40 - 60	°C
Melt Temperature	380 - 390	°C
Rear - Zone 1 Temperature	350 - 360	°C
Middle - Zone 2 Temperature	365 - 375	°C
Front - Zone 3 Temperature	380 - 395	°C
Nozzle Temperature	380 - 395	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	97	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	8700	MPa	ISO 527
Flexural Strength, 2 mm/min	169	MPa	ISO 178
Flexural Modulus, 2 mm/min	7700	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	99	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D638
Tensile Modulus, 5 mm/min	8700	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	161	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7600	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.86	g/cm³	ISO 1183
Melt Volume Rate, MVR at 400°C/10.0 kg	50	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 24 hrs	0.5 - 0.6	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.6	%	ISO 294
Moisture Absorption (23°C / 50% RH)	0.1 - 0.2	%	ISO 62
Water Absorption, (23°C/saturated)	0.2 - 0.23	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24 hrs)	<0.1	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.1	%	ASTM D570

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	>300	°C	ISO 75/Bf
HDT, 1.8 MPa, 3.2mm, unannealed	190	°C	ASTM D648
Vicat Softening Temp, Rate B/50	>300	°C	ISO 306
Vicat Softening Temp, Rate B/120	>300	°C	ISO 306
CTE, 23°C to 60°C, flow	3.0E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	4.1E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES