FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.78 | mm | UL 94 |
LNP THERMOCOMP LF006 compound is based on Polyetheretherketone (PEEK) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.78 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 875 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 117 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 13 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Front - Zone 3 Temperature | 380 - 400 | °C | |
Middle - Zone 2 Temperature | 380 - 400 | °C | |
Rear - Zone 1 Temperature | 370 - 380 | °C | |
Mold Temperature | 175 - 190 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 176 | MPa | ASTM D638 |
Tensile Strain, break | 2 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 13230 | MPa | ASTM D638 |
Flexural Stress | 245 | MPa | ASTM D790 |
Flexural modulus | 10750 | MPa | ASTM D790 |
Tensile Stress, break | 175 | MPa | ISO 527 |
Tensile Strain, break | 1.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 13100 | MPa | ISO 527 |
Flexural Stress | 263 | MPa | ISO 178 |
Flexural Modulus | 12700 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.54 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
Density | 1.53 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | >298 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | >298 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.62E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 4.68E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 4.84E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 875 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 117 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 13 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 176 | MPa | ASTM D638 |
Tensile Strain, break | 2 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 13230 | MPa | ASTM D638 |
Flexural Stress | 245 | MPa | ASTM D790 |
Flexural modulus | 10750 | MPa | ASTM D790 |
Tensile Stress, break | 175 | MPa | ISO 527 |
Tensile Strain, break | 1.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 13100 | MPa | ISO 527 |
Flexural Stress | 263 | MPa | ISO 178 |
Flexural Modulus | 12700 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.54 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
Density | 1.53 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | >298 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | >298 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.8E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 4.68E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 4.84E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.78 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.1 | % | |
Melt Temperature | 380 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 395 | °C | |
Middle - Zone 2 Temperature | 365 - 375 | °C | |
Rear - Zone 1 Temperature | 350 - 360 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 152 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 11100 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 217 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 10200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.53 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 2.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 4.6E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >280 | °C | ISO 75/Af |