ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+04 - 1.E+07 | Ω | ASTM D257 |
LNP THERMOCOMP LX04015 compound is based on Polyetheretherketone (PEEK) resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive, Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+04 - 1.E+07 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.1 | % | |
Melt Temperature | 380 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 395 | °C | |
Middle - Zone 2 Temperature | 365 - 375 | °C | |
Rear - Zone 1 Temperature | 350 - 360 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 200 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 13800 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 275 | MPa | ISO 178 |
Flexural Strain, break, 2 mm/min | 3.1 | % | ISO 178 |
Flexural Modulus, 2 mm/min | 11100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
Density | 1.34 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 5.4E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 300 | °C | ISO 75/Af |