LNP THERMOCOMP LX09404 compound is based on Polyetheretherketone (PEEK) resin containing 45% carbon fiber. Added features of this grade include: Electrically Conductive, High Modulus
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 828 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 93 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Middle - Zone 2 Temperature | 380 - 400 | °C | |
| Rear - Zone 1 Temperature | 370 - 380 | °C | |
| Mold Temperature | 175 - 190 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 280 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 41500 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 424 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 29650 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.47 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.41 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 332 | °C | ASTM D648 |