LNP™ THERMOCOMP™ Compound M10006P

LNP THERMOCOMP* M10006P compound is based on Polypropylene (PP) resin containing non-halogenated Flame retardant suitable for use in composites and extrusion.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Impregnation (composites)
Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
Good Processability
No PFAS intentionally added

Industry

Material previously used in

Industrial General

Applications

Possible usage of material

Chemical & industrial systems

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	2 - 4	Hrs
Barrel - Zone 1 Temperature	200 - 250	°C
Melt Temperature	230 - 300	°C

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	18	kJ/m²	ISO 180/1U

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	24	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.7	%	ISO 527
Tensile Modulus, 1 mm/min	2060	MPa	ISO 527
Flexural Strength, 2 mm/min	40	MPa	ISO 178
Flexural Modulus, 2 mm/min	1830	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate, MVR at 230°C/2.16 kg	70	cm³/10 min	ISO 1133

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES