LNP THERMOCOMP MB006HS compound is based on Polypropylene (PP) resin containing 30% glass bead. Added features of this grade include: Heat Stabilized, Healthcare.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 229 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 21 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 28 | MPa | ASTM D638 |
| Tensile Strain, break | 23.4 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2590 | MPa | ASTM D638 |
| Flexural Stress | 41 | MPa | ASTM D790 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 1 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 63 | °C | ASTM D648 |