LNP THERMOCOMP MF0049I compound is based on Polypropylene (PP) resin containing 20% glass fiber. Added features of this grade include: Flame Retardant, Impact Modified.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Compliant, 94V-0 Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.34 | % | SABIC method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 3.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.18E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 156 | °C | ISO 75/Af |