IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP MF006A compound is based on Polypropylene (PP) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 225 - 250 | °C | |
Front - Zone 3 Temperature | 240 - 250 | °C | |
Middle - Zone 2 Temperature | 215 - 225 | °C | |
Rear - Zone 1 Temperature | 195 - 205 | °C | |
Mold Temperature | 30 - 50 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 50 mm/min | 81 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 1.9 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 6500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 102 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 6200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.12 | % | SABIC method |
Density | 1.15 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Af |