IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 39 | J/m | ASTM D256 |
LNP THERMOCOMP MFB22EXJ compound is based on Polypropylene (PP) resin containing 10% glass fiber and 10% glass bead. Added features of this grade include: Easy Molding, Low Extractables, Healthcare, Food Contact compliant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 39 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 225 - 250 | °C | |
Front - Zone 3 Temperature | 240 - 250 | °C | |
Middle - Zone 2 Temperature | 215 - 225 | °C | |
Rear - Zone 1 Temperature | 195 - 205 | °C | |
Mold Temperature | 30 - 50 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 34 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 30 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.9 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 6.7 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 4080 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 50 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2970 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.05 | g/cm³ | ASTM D792 |
Melt Flow Rate, 210°C/5 kgf | 12 - 20 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 100 | °C | ASTM D648 |