IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
LNP THERMOCOMP MFB41I compound is based on Polypropylene (PP) resin containing 5% glass fiber, 20% glass bead. Added features of this grade include: Improved Impact.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 225 - 250 | °C | |
Front - Zone 3 Temperature | 240 - 250 | °C | |
Middle - Zone 2 Temperature | 215 - 225 | °C | |
Rear - Zone 1 Temperature | 195 - 205 | °C | |
Mold Temperature | 30 - 50 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 33 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 4.1 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2450 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 50 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.6 - 0.8 | % | SABIC method |
Density | 1.07 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 0.03 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 6.7E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |