IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
LNP THERMOCOMP MX95319 compound is based on Polypropylene (PP) resin containing 20% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 225 - 250 | °C | |
Front - Zone 3 Temperature | 240 - 250 | °C | |
Middle - Zone 2 Temperature | 215 - 225 | °C | |
Rear - Zone 1 Temperature | 195 - 205 | °C | |
Mold Temperature | 30 - 50 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 66 | MPa | ASTM D638 |
Tensile Strain, break | 3.1 | % | ASTM D638 |
Flexural Stress | 103 | MPa | ASTM D790 |
Flexural Modulus | 4130 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.04 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D955 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 145 | °C | ASTM D648 |