LNP THERMOCOMP OF006XA compound is based on branched Polyphenylene Sulfide (PPS) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 405 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 8 | J | ASTM D3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 31 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 315 - 340 | °C | |
| Front - Zone 3 Temperature | 330 - 345 | °C | |
| Middle - Zone 2 Temperature | 320 - 330 | °C | |
| Rear - Zone 1 Temperature | 305 - 315 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 129 | MPa | ASTM D638 |
| Tensile Strain, break | 1.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 12730 | MPa | ASTM D638 |
| Flexural Stress | 193 | MPa | ASTM D790 |
| Flexural Modulus | 11250 | MPa | ASTM D790 |
| Tensile Stress, break | 129 | MPa | ISO 527 |
| Tensile Strain, break | 1.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12480 | MPa | ISO 527 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Flexural Modulus | 11880 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.13 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ISO 294 |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 267 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.34E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 4.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.41E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.57E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 263 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 315 - 340 | °C | |
| Front - Zone 3 Temperature | 330 - 345 | °C | |
| Middle - Zone 2 Temperature | 320 - 330 | °C | |
| Rear - Zone 1 Temperature | 305 - 315 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 157 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11100 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 238 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 1.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 263 | °C | ISO 75/Af |