IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 395 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 68 | J/m | ASTM D256 |
LNP THERMOCOMP OF008G compound is based on linear Polyphenylene Sulfide (PPS) resin containing 15% glass fiber, 25% milled glass.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 395 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 68 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 315 - 320 | °C | |
Front - Zone 3 Temperature | 330 - 345 | °C | |
Middle - Zone 2 Temperature | 320 - 330 | °C | |
Rear - Zone 1 Temperature | 305 - 315 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 104 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 8840 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 157 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 9300 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow, 24 hrs | 0.2 - 0.5 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.8 - 1 | % | ASTM D955 |
Your PDF is downloading. Please wait.