LNP™ THERMOCOMP™ Compound OF00AN

LNP THERMOCOMP OF00AN compound is based Polyphenylene Sulfide (PPS) containing 50% glass fiber. Added features include: High Modulus, Impact Modified, Low Chloride content, Good Warpage Control, Inherently Flame Retardant. Excellent High Heat and Chemical Resistance and Good Metal Bonding Strength targeted for Nano-Molding Technology (NMT) applications.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Linear (PPS, Linear)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Flame Retardant
High stiffness/Strength
Low Warpage
Nano molding technology
No PFAS intentionally added
Thin Wall

Industry

Material previously used in

Electrical
Material Handling

Applications

Possible usage of material

Electrical
Electronics
nmt
nano molding technology
mobile phone antenna
laptop antenna
wearable device antenna
antenna split

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.9 GHz	4.3	-	SABIC method
Dissipation Factor, 1.9 GHz	0.005	-	SABIC method
Dielectric Constant, 5 GHz	4.3	-	SABIC method
Dissipation Factor, 5 GHz	0.0058	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.4	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	145	J/m	ASTM D256
Izod Impact, unnotched, 23°C	650	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 -40°C*	13.5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 -40°C*	50	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	15	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 140	°C
Drying Time	3 - 4	Hrs
Hopper Temperature	50 - 70	°C
Melt Temperature	310 - 330	°C
Front - Zone 3 Temperature	310 - 330	°C
Middle - Zone 2 Temperature	300 - 320	°C
Rear - Zone 1 Temperature	290 - 300	°C
Mold Temperature	135 - 160	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	203	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D638
Tensile Modulus, 5 mm/min	16700	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	285	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	15200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	205	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.8	%	ISO 527
Tensile Modulus, 1 mm/min	16800	MPa	ISO 527
Flexural Strength, 2 mm/min	290	MPa	ISO 178
Flexural Modulus, 2 mm/min	15400	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.7	g/cm³	ASTM D792
Melt Flow Rate, 315°C/5.0 kgf	30	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 315°C/5.0 kg	18	cm³/10 min	ISO 1133
Specific Gravity	1.7	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24hrs)	0.01	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.02	%	ISO 62-1
Water Absorption, (23°C/24hrs)	0.01	%	ASTM D570
Mold Shrinkage, flow	0.2 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	268	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	275	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	270	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	276	°C	ISO 75/Bf
CTE, -40°C to 90°C, flow	1.2E-05	1/°C	ASTM E831
CTE, -40°C to 90°C, xflow	4.1E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.3E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.0E-05	1/°C	ISO 11359-2
CTE, -40°C to 90°C, flow	1.3E-05	1/°C	ISO 11359-2
CTE, -40°C to 90°C, xflow	4.3E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	130	°C	UL 746B
Relative Temp Index, Mech w/impact	130	°C	UL 746B
Relative Temp Index, Mech w/o impact	130	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience