LNP™ THERMOCOMP™ Compound OFC08V

LNP THERMOCOMP OFC08V is a glass fiber reinforced Polyphenylene sulfide (PPS) compound. Added features include: high heat and chemical resistance, good warpage control and inherently flame-retardant, low flash and good processability, excellent LDS capability and plating performance, stable dielectric properties at various temperatures. Applications of this grade include 5G infrastructure and electronic components.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Linear (PPS, Linear)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dielectrics
Dimensional stability
Flame Retardant
High stiffness/Strength
High temperature resistance
Laser Direct Structuring
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Electrical

Applications

Possible usage of material

Antenna
Auto Electrical
Infrastructure
Sensor
Wireless Communications
mobile phone antenna
laptop antenna
lds
laser direct structuring
vcm
5g dipole antenna
dielectric
smt

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.9 GHz	4.05	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0045	-	SABIC method
Dielectric Constant, 5 GHz	4.05	-	SABIC method
Dissipation Factor, 5 GHz	0.0047	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.75	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	55	J/m	ASTM D256
Izod Impact, unnotched, 23°C	420	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	30	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	5.2	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	29	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 140	°C
Drying Time	3 - 4	Hrs
Hopper Temperature	50 - 70	°C
Melt Temperature	310 - 330	°C
Nozzle Temperature	310 - 330	°C
Front - Zone 3 Temperature	310 - 320	°C
Middle - Zone 2 Temperature	300 - 320	°C
Rear - Zone 1 Temperature	290 - 310	°C
Mold Temperature	135 - 160	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	131	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.5	%	ASTM D638
Tensile Modulus, 5 mm/min	13000	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	183	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	12000	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	130	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	13200	MPa	ISO 527
Flexural Strength, 2 mm/min	180	MPa	ISO 178
Flexural Modulus, 2 mm/min	12000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.69	-	ASTM D792
Density	1.69	g/cm³	ASTM D792
Water Absorption, (23°C/24hrs)	0.01	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.02	%	ISO 62-1
Water Absorption, (23°C/saturated)	0.03	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.01	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.01	%	ISO 62-4
Melt Flow Rate, 315°C/5.0 kgf	60	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 316°C/5.0 kg	36	cm³/10 min	ASTM D1238
Mold Shrinkage, flow	0.2 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	272	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	254	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	272	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Af
CTE, -40°C to 90°C, flow	1.9E-5	1/°C	ASTM E831
CTE, -40°C to 90°C, xflow	4.6E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.7E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.2E-5	1/°C	ISO 11359-2
CTE, -40°C to 90°C, flow	1.9E-5	1/°C	ISO 11359-2
CTE, -40°C to 90°C, xflow	4.5E-5	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES