LNP™ THERMOCOMP™ Compound OFC08XXP

LNP THERMOCOMP OFC08XXP compound is a 40% glass fiber reinforced polyphenylene sulfide. Added feature of this material include: High stiffness/strength, High flow, Low warpage, Impact resistant, Chemical resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Linear (PPS, Linear)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
High Flow
High stiffness/Strength
Impact resistant
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood
Energy Management
Industrial General

Applications

Possible usage of material

Electronic Components
Infrastructure
Power Manangement
Semiconductor
Structural Support
Wireless Communications
Structural
5g dipole antenna
smt connector
cooling fan

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.9 GHz	4.0	-	SABIC method
Dissipation Factor, 1.9 GHz	0.0042	-	SABIC method
Dielectric Constant, 5 GHz	4.0	-	SABIC method
Dissipation Factor, 5 GHz	0.0045	-	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	128	J/m	ASTM D256
Izod Impact, unnotched, 23°C	650	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	13	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	50	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	13	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	53	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 140	°C
Drying Time	3 - 4	Hrs
Hopper Temperature	50 - 70	°C
Melt Temperature	310 - 330	°C
Nozzle Temperature	310 - 330	°C
Front - Zone 3 Temperature	310 - 330	°C
Middle - Zone 2 Temperature	300 - 320	°C
Rear - Zone 1 Temperature	290 - 310	°C
Mold Temperature	135 - 160	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	190	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.0	%	ASTM D638
Tensile Modulus, 5 mm/min	15400	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	270	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	13800	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	190	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	15500	MPa	ISO 527
Flexural Strength, 2 mm/min	270	MPa	ISO 178
Flexural Modulus, 2 mm/min	14000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.66	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.02	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.01	%	ISO 62-4
Melt Flow Rate, 315°C/5.0 kgf	64	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.2 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	278	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	266	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	278	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	267	°C	ISO 75/Af
CTE
– -40°C to 90°C, flow	1.5E-5	1/°C	ASTM E831
– -40°C to 90°C, xflow	4.5E-5	1/°C	ASTM E831
– -40°C to 40°C, flow	1.5E-5	1/°C	ISO 11359-2
– -40°C to 40°C, xflow	4.2E-5	1/°C	ISO 11359-2
– -40°C to 90°C, flow	1.6E-5	1/°C	ISO 11359-2
– -40°C to 90°C, xflow	4.5E-5	1/°C	ISO 11359-2
– -40°C to 125°C, flow	1.6E-5	1/°C	ISO 11359-2
– -40°C to 125°C, xflow	5.0E-5	1/°C	ISO 11359-2

Register for High value Multi-Point Data