LNP™ THERMOCOMP™ Compound PDXE00715EES

LNP THERMOCOMP PDXE00715EES compound is based on Polyetherimide (PEI) resin containing 10% glass fiber. Added features of this grade include: Healthcare.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Healthcare/Formula lock
High stiffness/Strength
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

General Healthcare
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Surgical Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	52.9	J/m	ASTM D256
Izod Impact, unnotched, 23°C	687	J/m	ASTM D4812
*Izod Impact, unnotched 80104 +23°C*	37.2	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5.2	kJ/m²	ISO 180/1A
Multiaxial Impact	7.1	J	ASTM D3763
Multiaxial Impact	2.2	J	ISO 6603

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	121	°C
Drying Time (Cumulative)	4 - 6	Hrs
Melt Temperature	360 - 365	°C
Front - Zone 3 Temperature	365 - 376	°C
Middle - Zone 2 Temperature	354 - 365	°C
Rear - Zone 1 Temperature	343 - 354	°C
Mold Temperature	121 - 148	°C
Back Pressure	0.34 - 0.68	MPa
Screw Speed	60 - 100	rpm
Maximum Moisture Content	0.02	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Flexural Modulus, 1.3 mm/min, 50 mm span	5090	MPa	ASTM D790
Flexural Modulus, 2 mm/min	5084	MPa	ISO 178
Flexural Stress	202	MPa	ISO 178
Tensile Modulus, 5 mm/min	5022	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	129	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	129	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4.7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	6	%	ASTM D638
Tensile Modulus, 1 mm/min	4986	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	127	MPa	ISO 527
Tensile Stress, break, 5 mm/min	123	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4.5	%	ISO 527
Tensile Strain, break, 5 mm/min	5.8	%	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.35	g/cm³	ASTM D792
Specific Gravity	1.36	-	ASTM D792
Mold Shrinkage, flow, 24 hrs	2.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	2.4	%	ASTM D955
Moisture Absorption, (23°C/50% RH/24 hrs)	0.17	%	ASTM D570
Moisture Absorption (23°C / 50% RH)	0.29	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	205	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	211	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	213	°C	ISO 75/Bf
CTE, -30°C to 30°C, xflow	0.000046	1/°C	ASTM D696
CTE, -30°C to 30°C, flow	0.000032	1/°C	ASTM D696

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES