LNP THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 530 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 123 | MPa | ASTM D638 |
| Tensile Strain, break | 3.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 6350 | MPa | ASTM D638 |
| Flexural Stress | 179 | MPa | ASTM D790 |
| Flexural Modulus | 5600 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 203 | °C | ASTM D648 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 530 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 123 | MPa | ASTM D638 |
| Tensile Strain, break | 3.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 6350 | MPa | ASTM D638 |
| Flexural Stress | 179 | MPa | ASTM D790 |
| Flexural Modulus | 5600 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 203 | °C | ASTM D648 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | >1.E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+16 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0061 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.016 | - | IEC 60250 |
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Comparative Tracking Index, M | 450 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 3.6 | - | IEC 60250 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Compliant, 94HB Flame Class Rating | 0.75 | mm | UL 94 by SABIC-IP |
| Oxygen Index (LOI) | 24 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.2 | % | |
| Melt Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Front - Zone 3 Temperature | 250 - 280 | °C | |
| Middle - Zone 2 Temperature | 250 - 280 | °C | |
| Rear - Zone 1 Temperature | 250 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 70 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 125 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5800 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4750 | MPa | ISO 178 |
| Hardness, Rockwell L | 110 | - | ISO 2039-2 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.45 - 0.85 | % | SABIC method |
| Density | 1.23 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 8 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 206 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 212 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |