LNP™ THERMOCOMP™ Compound PF006U

LNP THERMOCOMP PF006U compound is based on Nylon 6 resin containing 30% glass fiber. Added features of this grade include: UV Stabilized.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added
Weatherable/UV stable

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Lighting

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity, ROA	>1.E+16	Ω	IEC 60093
Volume Resistivity	>1.E+16	Ω.cm	IEC 60093
Comparative Tracking Index	500	V	IEC 60112
Comparative Tracking Index, M	375	V	IEC 60112
Dielectric Strength, in oil, 3.2 mm	20	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	3.4	-	IEC 60250
Dissipation Factor, 1 MHz	0.016	-	IEC 60250
Relative Permittivity, 50/60 Hz	3.6	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.0061	-	IEC 60250

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94HB Flame Class Rating	1.5	mm	UL 94 by SABIC-IP
Oxygen Index (LOI)	25	%	ISO 4589
Glow Wire Flammability Index 650°C, passes at	2	mm	IEC 60695-2-12

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	117	J/m	ASTM D256
Izod Impact, unnotched, 23°C	827	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	9	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -20°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	55	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	11	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	9	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	90	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	75	kJ/m²	ISO 179/1eU
Multiaxial Impact	2	J	ISO 6603

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.2	%
Hopper Temperature	60 - 80	°C
Melt Temperature	260 - 290	°C
Rear - Zone 1 Temperature	250 - 280	°C
Middle - Zone 2 Temperature	260 - 290	°C
Front - Zone 3 Temperature	260 - 290	°C
Nozzle Temperature	250 - 280	°C
Mold Temperature	80 - 100	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	129	MPa	ASTM D638
Tensile Strain, break	2.8	%	ASTM D638
Tensile Modulus, 5 mm/min	8750	MPa	ASTM D638
Flexural Stress	201	MPa	ASTM D790
Flexural modulus	8960	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	144	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3.3	%	ISO 527
Tensile Modulus, 1 mm/min	9040	MPa	ISO 527
Flexural Stress	203	MPa	ISO 178
Flexural Modulus, 2 mm/min	8000	MPa	ISO 178
Hardness, Rockwell L	112	-	ISO 2039-2

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.36	g/cm³	ISO 1183
Density	1.36	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.86	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 1.2	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.17 - 0.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1 - 1.2	%	ISO 294
Mold Shrinkage on Tensile Bar, flow	0.2 - 0.4	%	SABIC method
Moisture Absorption (23°C / 50% RH)	1.53	%	ISO 62
Water Absorption, (23°C/saturated)	6.5	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	219	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	206	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	203	°C	ISO 75/Af
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	210	°C	ISO 75/Ae
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	220	°C	ISO 75/Be
Vicat Softening Temp, Rate B/120	215	°C	ISO 306
Vicat Softening Temp, Rate B/50	215	°C	ISO 306
CTE, -40°C to 40°C, flow	3.05E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.73E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	3.06E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.72E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, flow	2.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	8.5E-05	1/°C	ISO 11359-2
Thermal Conductivity	0.33	W/m-°C	ISO 8302

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES