LNP™ THERMOCOMP™ Compound PF008
LNP THERMOCOMP PF008 compound is based on Nylon 6 resin containing 40% glass fiber.
Product Family
- LNP™ COMPOUNDS AND PC COPOLYMER RESINS
Polymer Family
- Polyamide 6 (Nylon 6)
Processing Technology
- Injection Molding
Colors
All colors are customizable. Refer our ColorXpress tool to check color availability
Features
Key characteristics of the material- High stiffness/Strength
- No PFAS intentionally added
Industry
Material previously used in- Building Component
- Commercial Appliance
- Electrical
- Home Appliances
- Mobile Phone - Computer - Tablets
- Personal Accessory
- Sport/Leisure
Applications
Possible usage of material- Heavy Vehicles
Technical Datasheet Data
View different characteristics of the material at a standard test conditionsIMPACT
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 133 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 25 | J | ASTM D3763 |
| Multiaxial Impact | 21 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 92 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
INJECTION MOLDING
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
MECHANICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 183 | MPa | ASTM D638 |
| Tensile Strain, break | 3.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 12670 | MPa | ASTM D638 |
| Flexural Stress | 278 | MPa | ASTM D790 |
| Flexural Modulus | 9250 | MPa | ASTM D790 |
| Tensile Stress, break | 186 | MPa | ISO 527 |
| Tensile Strain, break | 3.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12990 | MPa | ISO 527 |
| Flexural Stress | 278 | MPa | ISO 178 |
| Flexural Modulus | 9530 | MPa | ISO 178 |
PHYSICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.98 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ISO 294 |
| Density | 1.46 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.26 | % | ISO 62 |
THERMAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 195 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 208 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 70 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B |
Related Documents
you can download all the related literature to this material here. If any other document is required, please contact usTechnical Data Sheets
Your PDF is downloading. Please wait.
Register for High value Multi-Point Data
- Access validated product data to streamline material selection
- Get inspired by innovative application ideas
- Register for high value multi-point data and a personalized experience