PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 843 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 138 | J/m | ASTM D256 |
LNP THERMOCOMP PX92248 compound is based on Nylon 6 resin containing 30% glass fiber. Added features of this grade include: Improved Impact, UV Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 843 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 138 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 265 - 275 | °C | |
Front - Zone 3 Temperature | 275 - 290 | °C | |
Middle - Zone 2 Temperature | 265 - 275 | °C | |
Rear - Zone 1 Temperature | 250 - 260 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 107 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 107 | MPa | ASTM D638 |
Tensile Strain, break | 2.5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 8840 | MPa | ASTM D638 |
Flexural Stress | 179 | MPa | ASTM D790 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 179 | MPa | ASTM D790 |
Flexural Modulus | 7220 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 7220 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.34 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 195 | °C | ASTM D648 |