LNP THERMOCOMP QF006 compound is based on Nylon 6/10 resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Hot-Wire Ignition (HWI), PLC 4 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1116 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 122 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 9 | J | ASTM D3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 71 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 150 | MPa | ASTM D638 |
| Tensile Strain, break | 3.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 8410 | MPa | ASTM D638 |
| Flexural Stress | 250 | MPa | ASTM D790 |
| Flexural Modulus | 7860 | MPa | ASTM D790 |
| Tensile Stress, break | 153 | MPa | ISO 527 |
| Tensile Strain, break | 3.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8800 | MPa | ISO 527 |
| Flexural Stress | 219 | MPa | ISO 178 |
| Flexural Modulus | 7800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.309 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.17 - 0.18 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.98 - 0.99 | % | ISO 294 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.33 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 207 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.05E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.27E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 3.06E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.27E-05 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.