LNP THERMOCOMP QF00A compound is based on Nylon 6/10 resin containing 50% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1305 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 160 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 75 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 181 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 181 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 18680 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 280 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 285 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11440 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 181 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 181 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15510 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 12870 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.6 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.21 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.18 - 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 1.5 | % | ASTM D955 |
| Density | 1.6 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.28 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 221 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 213 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 95 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 19 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 181 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 265 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.4 | % | SABIC method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.