LNP THERMOCOMP RC003SXS compound is based on Nylon 6/6 resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.78E+05 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | 1.78E+05 | Ω | IEC 60093 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP |
| Oxygen Index (LOI) | 28 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 3 | kJ/m² | ISO 180/1A |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 320 - 360 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Front - Zone 3 Temperature | 320 - 360 | °C | |
| Middle - Zone 2 Temperature | 320 - 360 | °C | |
| Rear - Zone 1 Temperature | 280 - 320 | °C | |
| Hopper Temperature | 60 - 90 | °C | |
| Mold Temperature | 80 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 170 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 230 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10000 | MPa | ISO 178 |
| Hardness, Rockwell L | 105 | - | ISO 2039-2 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.1 - 0.2 | % | SABIC method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 5.5 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 2.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.1E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 255 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 252 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 250 | °C | ISO 75/Ae |